Double-faced Adhesive Tape

Nonwoven-fabric/film base material double-faced tape

Grade Compo
-sition
(Base
/Adhesive)
No. of rele
-ase liners
Standard size Color Initial
Adhesion

 adhesion (N
/25mm)

JIS
holding per
-for
-mance
(mm)
Advantages Applications
Thick
-ness
(mm)
Width
(mm)
Length
(m)
570E Nonwoven
-fabric
/Acrylic

1

0.12

5
-
1,200

20
/50

Trans -licent

o

18.3

0.2

Excellent adhesion and weather resistance

For general adhesion

570M Nonwoven
-fabric
/Acrylic

1

0.12

5
-
1,200

20
/50

Trans -licent

o+

11.8

0.3

Excellent initial adhesion and low-temperature resistance

For splicing of paper film

575F Nonwoven
-fabric
/Acrylic

1

0.16

5
-
1,200

20
/50

Trans -licent

o

22.1

0.3

Excellent adhesion and weather resistance

For adhesion of aluminum nameplates

5753E Nonwoven
-fabric
/Acrylic

1

0.20

5
-
1,200
/
10
-
1,200

20
/50

Trans -licent

o

20.4

0.4

Excellent adhesion to rough surfaces and weather resistance

For setting of foamed rubber

5760E Nonwoven
-fabric /Acrylic

1

0.14

5
-
1,200

20
/50

Trans -licent

o

18.1

0.3

Adhesion to olefin plastics such as PP, PE, and EPDM

For adhesion of resin nameplates

5761E Nonwoven
-fabric
/Acrylic

1

0.12

5
-
1,200

20
/50

Trans -licent

o

18.3

0.2

Excellent adhesion and weather resistance

For adhesion of resin nameplates

575E Nonwoven
-fabric
/Acrylic

1

0.14

5
-
1,200

20
/50

Trans -licent

o

18.1

0.3

Excellent adhesion and weather resistance

For setting of cushon materials and seal materials

5782 Nonwoven
-fabric
/Acrylic

1

0.13

5
-
1,200

20
/50

Trans -licent

o

18.6

*0.2

Good adhesion to foamed urethane
Excellent repulsion resistance

For adhesion of formed urethane

584 Tissue
paper
/Rubber

1

0.13

7
-
1,200

30
/33
/60

White

o

18.6

0.3

Excellent initial adhesion and holding performance

For attaching of golf club grips
For attaching of printed boards

595TF Tissue
paper
/Acrylic

1

0.17

5
-
1,200

20
/50

Trans -licent

o

20.6

0.2


Strong base material

For setting flooringsand recycling

560 PP
/Acrylic

1

0.13

5
-
1,200

20
/50

Trans -licent

o+

7.8

0.2

Strong base material
Excellent removability

For attaching of rearview mirrors
For setting of cushions and floorings

Notes:

1.  Adhesion is measured by a 180-degree peeling resistance test according to JIS Z0237. (Items identified by "*" are subject to a 90-degeree peeling resistance test.)
2.  Initial adhesion indicates the degree of adhesion. o+: Excellent, o: Good
3.  JIS holding performance is measured at 40'C according to JIS Z0237. (Items identified by "*" are measured under 80'C temperature and 500 g load conditions.

Foam base material double-faced tape

Grade Compo
-sition
(Base
/Adhesive)
No. of release liners Standard size Color Initial
Adhesion
Adhesion
(N
/25mm)
JIS
holding per
-for
-mance
(mm)
Advantages Applications
Thick
-ness
(mm)
Width
(mm)
Length
(m)
516L  Special
polye
-thylene
foam    
/Acrylic

1

1.3

7
-
950

10
/60

Black

o+

10.1

*0.4

Excellent adhesion to rough surfaces, holding performance, and weather resistance

For attaching of vehicle exteriors (e.g., side molding and emblems)

516K

1

1.1

7
-
950

30
/50

Black

o+

11.3

*0.3

516H

1

1.8

7
-
950

30

Black

o+

13.2

*0.5

Excellent weather resistance and adhesion to foams

5162

1

0.9

7
-
950

10
/30
/60

Black

o+

*11.5

*0.4

517

1

0.9

7
-
950

10
/30
/60

Black

o

*15.9

0.3

Excellent adhesion to rough surfaces, holding performance
Application to various adherends

For attaching of vehicle exteriors

For setting of housing components

532S

1

1.1

10
-
950

10

White

o+

*32.8

0.7

Excellent initial adhesion and adhesion to rough surfaces

For temporary setting of building interior and exterior boards

533 polye
-thylen
e foam
/Acrylic

1

0.43

10
-
950

15
/25

White

o

*18.8

0.2

Excellent holding peformance

For general adhesion

535 .536  Special polye
-thylene foam    
/Rubber

#535 1 #536 2

1.1

 10
-
950
450

10

1

White

o

*18.6

0.2

Excellent adhesion to rough surfaces
Excellent holding performance at ordinary temperature

For setting of hook hangers

538 Special
polye
-thylene
foam    
/Acrylic

1

1.1

7
-
950

10

White

o+

*23.5

0.2

Excellent adhesion to rough surfaces, holding performance
Application to various adherends

For attaching of cord clamps

2310 Special
polye
-thylene
 foam      
/Acrylic

1

2.0

3.0

5.0

450

1

Yellow
 Gray

o

*26.5

1.0

Excellent cushioning performance, holding performance, adhesion to rough surfaces

For attaching of mirrors on washstands and furniture

Notes:

1.  Adhesion is measured by a 180-degree peeling resistance test according to JIS Z0237. (Items identified by "*" are subject to a 90-degeree peeling resistance test.)
2.  Initial adhesion indicates the degree of adhesion. o+: Excellent, o: Good
3.  JIS holding performance is measured at 40'C according to JIS Z0237. (Items identified by "*" are measured under 80'C temperature and 500 g load conditions.

Cloth double-faced tape

Grade Compo
-sition
(Base /Adhe
-sive)
No.
of rele
-ase liners
Standard size Color Initial Adhe
-sion
Adhe
-sion
(N
/25mm)
Shear adhe
-sion
(N/cm2)
Advantages Applications
Thick
-ness
(mm)
Width
(mm)
Length
(m)
610 Cloth
/Rubber

1

0.55

50

15

Beige

o+

6.37

34.3

Flexible and excellent adhesion to rough surfaces

For attaching of carpets and mats
For attaching of freezer case door gaskets

615 Cloth
/Rubber

1

1.0

30

15

Black

o+

22.0

44.1

Excellent adhesion to rough surfaces, water resistance, and weather resistance

For temporary setting of building materials
For sealing corrugated roof joints

Note:

1.  Adhesion is measured by a 180-degree peeling resistance test according to JIS Z0237. (Items identified by "*" are subject to a 90-degeree peeling resistance test.)
2.  Initial adhesion indicates the degree of adhesion. o+: Excellent, o: Good

Position-adjustable double-faced tape

Grade Compo
-sition
(Base /Adhesive)
No. of rele
-ase liners
Standard size Color Initial Adhe
-sion
Adhesion
(N
/25
mm)
Shear adhe
-sion
(N/cm2)
Advantages Applications
Thick
-ness
(mm)
Width
(mm)
Length
(m)
530 Special PE foam
/Acrylic

1

0.8

20
-
360

20

White

o

13.7

31.9

Position-adjustable

Excellent adhesion to rough surfaces and repulsion resistance

setting of flooring

Notes:
1.  Adhesion is measured by a 180-degree peeling resistance test according to JIS Z0237. (Items identified by "*" are subject to a 90-degeree peeling resistance test.)
2.  Initial adhesion indicates the degree of adhesion. o+: Excellent, o: Good

 Construction double-faced tape

Grade Composition
(Base
/Adhesive)
Standard size Color

 T peeling resis
-tance
(N/cm)

Shear adhe
-sion
(N/cm2)

Tensile adhe
-sion
(N/cm2)

Heat resis
-tance, 'C

Advantages Applications
Thick
-ness
(mm)
Width
(mm)
Length
(m)
5101A Special Acrylic
/Acrylic

1.09

Approx. 10 to 500 mm (1 mm increment)

2
/10
/20

White

35

100

100

200

Excellent weather resistance and heat resistance

Flexible jointing, beautiful finish, and easy jointing (#5101A and #5106A feature excellent adhesion to rough surfaces)

 For assembly of doors and exterior materials in building

For setting of interior and exterior materials in housing and buildings

For attaching of vehicle interior and exterior components

For assembling and setting of metallic components

For assembling and setting of signboards and living goods

5102A Special Acrylic
/Acrylic

0.29

2
/40

White

10

140

120

200

5104A Special Acrylic
/Acrylic

0.49

40

White

20

120

100

200

5106A Special Acrylic
/Acrylic

0.69

30

White

25

110

100

200

SEKISUI SJ Acrylic

0.60

20
/24
/25
/30
/50
/100

40

-

18

100

-

-

Shortening of construction schedule thanks to adhesive-free construction

For reforming of housing and building walls

 Note
1: Adhesion is measured by a 180-degree peeling resistance test according to JIS Z0237. (Items identified by "*" are subject to a 90-degeree peeling resistance test.)

Acrylic waterproof tape for housing opening

Grade Composition
(Base
/Adhesive)
No. of release liners Standard size Color Initial Adhesion Adhesion
(N
/25mm)

 Ball tack
(1
/32')

Advantages Applications
Thick
-ness
(mm)
Width
(mm)
Length
(m)

Waterproof Double-faced Tape 5600

polye
-thylene cloth
/Acrylic

1

0.23

50
/75
/100

20

Trans -licent

o

22.0

30

Stable adhesion to metallic and olefin products under low to high temperature conditions

Excellent long-term stability

For adhesion of sash and moisture-permeable sheet at housing opening to ensure waterproofing

Waterproof Tape 7300 (single-faced adhesive tape)

polye
-thylene
cloth
/Acrylic

-

0.17

50
/75
/100

20

Yellow

o

19.0

28

Notes:
1.  Adhesion is measured by a 180-degree peeling resistance test according to JIS Z0237. (Items identified by "*" are subject to a 90-degeree peeling resistance test.)
2.  Initial adhesion indicates the degree of adhesion. o+: Excellent, o: Good

 

TACKWELL tape

Grade Composition
(Base /Adhesive)
No. of release liners Standard size Color Peeling resis
-tance
(N/25mm)
All light trans
-mission (%)
Haze
(%)
Advantages Applications
Thick
-ness
(mm)
Width
(mm)
Length
(m)
TACKWELL
150R
PET
/Acrylic

-

0.010

300
-
1000

150

-

2.4

93.5

2.7

Ultra thin-film, clean products
Re-adhesion after lamination
Excellent transparency and high durability

For protection of photo masks

TACKWELL
157R-N4
PET
/Acrylic

-

0.010

2.5

90.5

2.3

TACKWELL
155RFP
PET
/Acrylic

-

0.020

3.9

91.9

1.3

TACKWELL
157RSD
PET
/Acrylic

-

0.010

2.2

92.8

2.1

TACKWELL
157RSD-N4
PET
/Acrylic

-

0.010

2.3

92.8

2.1

TACKWELL
157RSD-S
PET
/Acrylic

-

0.012

2.5

92.8

2.1

TACKWELL
155RAS-ST
PET
/Acrylic

-

0.010

2.2

94.3

2.0

TACKWELL
157RASD
PET
/Acrylic

-

0.012

2.1

92.8

2.0

Note
1: Adhesion is measured by a 180-degree peeling resistance test according to JIS Z0237. (Items identified by "*" are subject to a 90-degeree peeling resistance test.)

Adhesion is measured by a 180-degree peeling resistance test according to JIS Z0237. (Items identified by "*" are subject to a 90-degeree peeling resistance test.)

 Thin-film masking tape

Grade Compo
-sition
(Base /Adhesive)
No. of rele
-ase liners
Standard size Color Peeling resis
-tance
(
N /25mm)
Light trans
-mission
(%)
Haze
(%)
Advantages Applications
Thick
-ness
(mm)
Width
(mm)
Length
(m)

Masking Tape 3250A

PET
/Acrylic
-

0.014

300
-
1000

200
-
360

-

0.13

92.3

4.2

 Ultra thin, weak adhesion, and reusable
High transparenc

For protection of resist layers

Masking Tape 3700

PET
/Acrylic
-

0.020

0.50

91.9

4.0

Note:
Adhesion is measured by a 180-degree peeling resistance test according to JIS Z0237. (Items identified by "*" are subject to a 90-degeree peeling resistance test.)

 


References
Surface Protection
Double-faced Adhesive Tape
Electrical Insulation Tape
Printing Process Tape
Aluminum Tape

Page Top

Privacy Policy Contact
Copyright (C) 2007 SEKISUI CHEMICAL CO., LTD.